Product Details:
Payment & Shipping Terms:
|
| Material: | KDP DKDP Non-Linear Crystal | Transmitting Range(nm): | 200~2150 |
|---|---|---|---|
| Absorption(%/cm): | 0.5 | Origin: | China |
| Delivery: | 1-4 Weeks | Shipment: | Express,DHL.Fedex |
| Packing: | Individual Container For Each Substrate, Packed In Bag Filled With Inert Gas. | DAMAGETHRESHOLD: | 1GW/cm2 For 1064nm, 10ns, 10Hz (uncoated) |
| High Light: | DKDP Nonlinear Crystal,KDP Nonlinear Crystal,1GW/cm2 dkdp crystal |
||
KDP DKDP Non-Linear Crystal
KDP and DKDP crystals are developed by water-solution method and can grow up to very big size. Therefore, they are good options for low-cost and large-size finished non-linear components, e.g. for frequency-doubling (SHG), frequency-tripling (THG) and frequency- quadrupling (FHG) of Nd:YAG laser at 1064nm.
Characterized by good UV transmission, high damage threshold, and high birefringence, Potassium Dihydrogen Phosphate (KDP) and Potassium Dideuterium Phosphate (DKDP ) are among the most widely-used commercial NLO materials, though their NLO coefficients are relatively low. They are usually used for the doubling, tripling and quadrupling of Nd:YAG laser at room temperature. They are also excellent E-O crystals with high E-O coefficients, widely used as electro-optical modulators, such as Q-switches, Pockels Cells, etc.
CRYSTRO can offer:
|
Crystal |
DKDP(KD*P) |
KDP |
ADP |
|
|
Transmitting Range(nm): |
200~2150 |
180~1550 |
180~1500 |
|
|
Absorption(%/cm): |
0.5 |
3 |
- |
|
|
Nonlinear Optical Coefficient (pm/V): |
0.40 |
0.43 |
0.52 |
|
|
Damage Threshold: (GW/cm2 @1064nm) |
5 |
5 |
6 |
|
|
Refractive Indices: |
@1064nm |
no=1.4931 |
no=1.4942 |
no=1.5071 |
|
ne=1.4583 |
ne=1.4603 |
ne=1.4685 |
||
|
@532nm |
no=1.5074 |
no=1.5129 |
no=1.5280 |
|
|
ne=1.4683 |
ne=1.4709 |
ne=1.4819 |
||
|
@355nm |
no=1.5257 |
no=1.5317 |
no=1.5487 |
|
|
ne=1.4833 |
ne=1.4846 |
ne=1.4994 |
||
|
@266nm
|
no=1.5539
|
no=1.5599
|
no=1.5797
|
|
|
ne=1.5071
|
ne=1.5105
|
ne=1.5261
|
||
|
Sellmeier Equations: (l in µm) |
N2 = A + B / (l2 - C) + Dl2/(l2- E) |
|||
|
A |
no |
2.2409 |
2.2576 |
2.3041 |
|
ne |
2.1260 |
2.1295 |
2.1643 |
|
|
B |
no |
0.0097 |
0.0101 |
0.0111 |
|
ne |
0.0086 |
0.0097 |
0.0097 |
|
|
C |
no |
0.0156 |
0.0142 |
0.0133 |
|
ne |
0.0120 |
0.0014 |
0.0129 |
|
|
D |
no |
2.2470 |
1.7623 |
15.1086 |
|
ne |
0.7844 |
0.7580 |
5.8057 |
|
|
E |
no |
126.9205 |
57.8984 |
400.0000 |
|
ne |
123.4032 |
127.0535 |
400.0000 |
|
|
Crystal |
KD*P(DKDP) |
KDP |
ADP |
|
Crystal Structure: |
|
||
|
Density(g/cm3): |
2.355 |
2.332 |
1.799 |
|
Color: |
Colorless |
||
|
Hygroscopic Susceptibility |
High |
||
|
Thermal Conductivity(10-2W/cm·K): |
k11=1.9;k33=2.1 |
- |
- |
|
Thermal Expansion Coefficients(10-5/K): |
a11=1.9;a33=4.4 |
- |
- |