Product Details:
Payment & Shipping Terms:
|
| Material: | Dia 5mm TGG Rod With High Power Low Absorption Loss Magneto Optical Crystals | Diameter: | 5mm,6mm,7mm,10mm,12mm |
|---|---|---|---|
| Chemical Formula: | =TB3Ga5O12 | Advantage: | High Power,Low Absoprtion Loss |
| Lattic Value: | A=12.355Å | Extinction Ratio: | <40dB |
| Brand Name: | CRYSTRO | Origin: | China |
| High Light: | Dia 5mm TGG Rod,Low Absorption Loss TGG Rod,REACH TGG crystal rod |
||
Dia 5mm TGG Rod With High Power Low Absorption Loss Magneto Optical Crystals
The terbium gallium garnite (TGG) crystal has high magnetooptic constant, low optical loss, high thermal conductivity and high laser damage threshold.TGG single crystal is the best magneto-optical material for making Faraday polarizers and isolators with applicable wavelength of 400~1100nm(not including 470~500nm).
The TGG crystal possesses a large Verdet constant (35 RadT−1m−1 at 1064 nm), high thermal conductivity (7.4 Wm−1K−1), low optical losses (< 0.1%/cm) and high laser damage threshold (> 1 GW/cm2).
Features:
CRYSTRO supply TGG crystal with:
| Orientation | [111] within ±15 arc min |
| Wave Front Distortion | <1/8 wave |
| Extinction Ratio | >35dB |
| Diameter Tolerance | +0.00mm/-0.05mm |
| Length Tolerance | +0.2mm/-0.2mm |
| Chamfer | 0.10mm@45º |
| Flatness | <1/10 wave at 633nm |
| Parallelism | < 30 arc Seconds |
| Perpendicularity | < 5 arc min |
| Surface Quality | 10/5 Scratch/Dig |
| AR Coating | <0.2% |
| Large Dimensions of Crystals | 2.0--76 mm in diameter |
Main Properties:
| Chemical Formula | TB3Ga5O12 |
| Lattic Parameter | a=12.355Å |
| Growth Method | Czochralski |
| Density | 7.13g/cm3 |
| Mohs Hardness | 8.0 |
| Melting Point | 1725℃ |
| Refractive Index | 1.954 at 1064nm |