Product Details:
Payment & Shipping Terms:
|
| Type: | TSAG Rod | Diameter: | 3inch |
|---|---|---|---|
| Diameter Tolerance: | +0/-0.05mm | Length Tolerance: | +/-0.2mm |
| Extinction Ratio: | Up To 35dB | Surface Quality: | 10-5 |
| AR Coating: | 405-980nm/1064nm | Wave Front Distortion: | <1/8 Wave |
| High Light: | gadolinium gallium garnet,ggg substrate,TSAG Optically Active Crystals |
||
TSAG Crystals For Faraday Isolator 1064nm 800nm 680nm AR Coating
Description:
TSAG is perfect magneto optical crystal which can be used in visible and infrared wavelength regions. Good thermal and mechanical properties make TSAG very reliable material suitable for next generation fiber lasers. Compared to TGG, TSAG has about 20% higher Verdet constant and about 30% lower absorption at 1064 nm.
Features:
Large Verdet constant(48 radT-1m-1 at 1064 nm),about 20% higher than that of TGG;
Low absorption(＜3000 ppm/cm at 1064 nm),about 30% less than that of TGG
High power compliant;
Low thermally-induced birefringence;
Making the isolator small.
Applications:
Faraday isolator based on TSAG crystal for high power lasers
Imaging applications:Scintillation properties of TSAG crystal for imaging applications
Main Properties:
| Transmittance Range(bulk/uncoated) | 400-1600nm |
| Crystal Structure | Cubic,Space group Ia3d |
| Chemical Formula | Tb3Sc2Al3O12 |
| Lattice Parameter | a=12.3Å |
| Growth Method | Czochralski |
| Density | 5.91g/cm3 |
| Melting Point | 1970℃±10℃ |
CRYSTRO supply TGG crystal with:
| Orientation | ±15′ |
| Wavefront Distortion | ＜λ/8 |
| Extinction Ratio | ＞30dB |
| Diameter Tolerance | +/-0.05mm |
| Length Tolerance | +/-0.1mm |
| Chamfer | 0.1mm @ 45° |
| Flatness | ＜λ/10 at 633nm |
| Parallelism | ＜3′ |
| Perpendicularity | ＜5′ |
| Surface Quality | 10/5 |
| AR coating | ＜0.3% @ 1064nm |