Product Details:
Payment & Shipping Terms:
|
| Material: | 6inch Diameter LiNbO3 E-O NLO Crsytal Wafer | Crystal Sturucture: | Trigonal, Space Group R3c, Point Group 3m |
|---|---|---|---|
| Orientation: | Z-cut, Y-cut 36° Off, Y-cut 64° Off, Y-cut 128° Off | Melting Point: | 1253℃ |
| Mohs Hardness: | 5 | Primary Orientation Flat: | 22mm+/-2mm (3-inch) 32mm+/-2mm (4-inch) |
| Standard Size: | φ6" (150mm) +/-0.3mm | Curie Temperature: | 1142℃ +/-0.7℃ |
| High Light: | 6 Inch Diameter LiNbO3 Crystal,NLO Crystal Wafer,Nonlinear Optical Grade Crystal |
||
6inch Diameter LiNbO3 E-O NLO Crsytal Wafer
LiNbO3 is a nonlinear optical grade crystal, it widely used in parametric oscillators, frequency doubling, acousto-optic devices, optical modulators. MgO-doped LiNbO3 can effectively increase the damage threshold of the LiNbO3 crystal..
MgO:LiNbO3 (Magnesium Oxide Doped Lithium Niobate) crystal has similar effective nonlinear coefficients to pure LiNbO3 and exhibits higher optical damage threshold.
Both pure LN and MgO doped LN (MgO:LN) crystals with gold coatings on side faces for electrodes are available
MgO doped LiNbO3 (MgO:LN) has similar linear optical properties to pure LiNbO3, but the photorefractive damage threshold is much higher.
Crystro's LiNbO3 crystal is grown by Czochralski method.Max diameter reach 6inch,it's now the biggest size in this filed,we can custom size and specs ,rougness<0.5nm.Magneto-optical single crystals like GGG,SGGG,TGG,TSAG are our main products.
Crystro provides:
LiNbO3 Crystal Applications:
1. Pockels Cells
2. Q-switches
3. Phase modulators
4. Surface acoustic wave(SAW) wafers
Basic Properties of LiNbO3:
| Growth method | Czochralski method |
| Crystal structure | Trigonal system |
| Lattice constant | a=b=5.148Å c=13.863 Å |
| Melting point | 1250℃ |
| Curie temperature | 1142 ℃ |
| Density | 4.64 g/cm3 |
| Mohs Hardness | 5 |
| Spectral transmission range | 0.4-2.9um |
| Refractive index | No=2.286 ne=2.203 (632.8nm) |
| Nonlinear coefficient | D33=34.45, d31=d15=5.95, d22=13.07 (PMV-1) |
| Electro-optic coefficient | γ13=8.6,γ22=3.4,γ33=30.8,γ51=28.0,γ22=6.00(pmv-1) |
| Spectral transmission range | 370 - 5000nm >68% (632.8nm) |
| Thermal expansion coefficient | A11=15.4 x 10-6/k, a33=7.5 x 10-6/k |
CRTSTRO can offer:
| Optical grade LiNbO3 | SAW grade LiNbO3 | |
| Orientation | X-cut, Z-cut (+/-0.2°) | Z-cut, Y-cut, |
| Y-cut 36° off, Y-cut 64° off, Y-cut 128° off | ||
| Primary Orientation Flat | 22mm+/-2mm (3-inch) | 22mm+/-2mm (3-inch) |
| 32mm+/-2mm (4-inch) | 32mm+/-2mm (4-inch) | |
| Standard Size | φ3"(76.2mm) +/-0.3mm | φ3" (76.2mm) +/-0.3mm |
| φ4" (100mm) +/-0.3mm | φ4" (100mm) +/-0.3mm | |
| φ6" (150mm) +/-0.3mm | φ6" (150mm) +/-0.3mm | |
| 10x10mm +/-0.1mm | 10x10mm +/-0.1mm | |
| Or others | Or others | |
| Thickness | 500μm +/-20μm | 500μm +/-20μm |
| 1000μm +/-20μm | 1000μm +/-20μm | |
| 350μm +/-20μm | 350μm +/-20μm | |
| Polishing | Single or Both side polished | Single or Both side polished |
| Surface Finish: 20/10 or 10/5 | Surface Finish: 20/10 or 10/5 | |
| TTV | ≤10um | ≤10um |
| Curie temperature | 1142℃ +/-0.7℃ | 1142℃ +/-3℃ |
| Edge chamfer | Edge rounding | Edge rounding |